张楼英，舒希勇，孙少东，张殿菊，张明生 (1.淮安信息技术学院，江苏 淮安 223003；2.淮安市创新自动化设备有限公司，江苏 淮安 223003)

摘要：从耐腐蚀性能的角度讨论了地锚拉杆镶嵌锻造的必要性。拉伸试验表明，地锚拉杆镶嵌锻造后，实用强度达不到设计要求的28.8 kN，断裂部位发生在拉杆镶嵌锻造部分，且靠近锁紧扣孔口。对拉杆镶嵌锻造部分的前后组织进行了金相观察，结果显示，拉杆冷变形后的细长晶粒经镶嵌锻造后重新转变成了等轴晶粒，产生了再结晶，冷变形强化效果消失是导致其实用强度下降的根源。进一步研究表明，拉杆产生再结晶是由高温锁紧扣锻坯热传导致其温度升高造成的。故镶嵌锻造前，在拉杆镶嵌锻造部分浸涂一定比例的混合液，使拉杆镶嵌锻造后的温度低至再结晶温度以下。采用此方法后的拉伸实验结果表明，地锚拉杆镶嵌锻造后实用强度未明显下降，金相分析也表明未产生再结晶。

关键词：地锚拉杆；金属再结晶；镶嵌锻造；实用强度
Study on recrystallization of earth anchor rods after mosaic forging
Zhang Louying, Shu Xiyong, Sun Shaodong, Zhang Dianju, Zhang Mingsheng
(1.Huaian College of Information Technology, Huaian 223003, China；2. Huaian Innovative Automation Equipment Co., Ltd., Huaian 223003, China)
Abstract: For corrosion resistance of earth anchor rods, the necessity of mosaic forging was investigated. Tensile tests show that the utility strength of earth anchor rods is below 28.8 kN after mosaic forging, and failed to satisfy the design standard. Furthermore, the fracture occurs in the mosaic forging part of anchor rods near to the shackle porthole. The microstructure of anchor rods was examined by optical microscope (OM). The results show that the elongated grains induced by cold deformation transform into equiaxed grains after mosaic forging, where recrystallization occurs. Thus, work hardening after cold deformation disappears which resulting in the degradation of utility strength. Then, it is believed that the temperature rise caused by heat conduction from the shackle is the main reason for recrystallization. Therefore, with earth anchor rods dip coating into mixed liquid with fixed proportion before mosaic forging, the temperature after mosaic forging decreases below the recrystallization temperature. The following tensile tests show that no obvious degradation in utility strength is observed after mosaic forging. At the same time, recrystallization is also not found by OM.
Key words: earth anchor rod metal recrystallization mosaic forging utility strength

联系我们：北京立基文化传播有限责任公司传播有限责任公司；010-57157202

国际杂志发行和广告代理：《International Sheet Metal Reviews 国际钣金评论》——欧洲板材展，亚洲板材展官方刊物；《锻压技术》《锻压装备与制造技术》——中国核心刊物；《E-铸锻周刊》《E-冲钣周刊》美国《锻造》《铸造管理与技术》；印度《今日锻造》， 捷克《锻造》，台湾《锻造》

2016展览和会议组织：2016印度成形技术与机床工具展；2016加拿大金属成形展Fabtech Canada；2016SAE美国汽车制造年会及零部件展；2016墨西哥金属成形展Fabtech Mexico；2016中国国际冲钣技术与装备研讨会；2016重庆锻造厂长(经理)技术交流会；2016立嘉国际冲压、锻压、钣金展览会 2016广州机床模具展；2016英国国际工业分包展览会；2016特种锻造技术工艺培训；2016俄罗斯国际汽车零配件展；2016法兰克福汽车零部件展；2016法国巴黎国际工业零配件展览会；2016欧洲金属板材加工技术展览会（EUROBLECH 2016）；2016第20届巴西锻造会议/第19届板材成形会议/第12届粉末冶金会议；2016巴西金属成形展；2016上海国际工业零部件及分承包展；2016第六届亚洲锻造会议；2016北美国际金属加工展览会（FABTECH 2016）；2016泰国金属加工展（Metalex 2016）